Dysprosium Modification of Cobalt Ferrite Ionic Magnetic Fluids
Dysprosium composite cobalt ferrite ionic magnetic fluids were prepared by precipitation in the presence of Tri-sodium citrate. Influence of dysprosium modification on magnetic property is studied. The result shows that magnetic response toward exterior magnetic field can be improved by adding Dy3+. Studies also show that the increase of reaction temperature may improve the modification effect of dysprosium. By adding dysprosium ions, the average diameter of the magnetic nanoparticles will be decreased evidently. It is clear that the particles appear as balls, Cobalt ferrite with sizes of 12-15 nm, rare earth composite cobalt ferrite with sizes of 6-8 nm.
作 者： JIANG Rong-li LIU Yong-chao GENG Quan-rong ZHAO Wen-tao 作者單位： School of Chemical Engineering and Technology,China University of Mining &Technology,Xuzhou,Jiangsu 221008,China 刊 名： 中國礦業大學學報（英文版） ISTIC EI 英文刊名： JOURNAL OF CHINA UNIVERSITY OF MINING & TECHNOLOGY 年，卷(期)： 2005 15(4) 分類號： O648.15 關鍵詞： cobalt ferrite magnetic fluids dysprosium modification mechanism magnetic property【Dysprosium Modification of Cobalt Fe】相關文章：
Modification on the conventional procedure to measure AOC in drinking water04-25
UV/Fenton體系中Fe2+/Fe3+的相互轉化規律04-25
Adsorption of As on hydroxy-Fe-montmorillonite complexes04-27
[{Fe(Salen)}3(Fe(CN)6}(MeOH)2]n·3nH2O的磁性研究04-26
Fe salts as catalyst for the wet oxidation of o-chlorophenol04-26
Catalytic dechlorination of o-cllorophenol by nanoscale Pd/Fe04-25
Fe3+對脆桿藻增殖的影響04-26
Fe/Mo多層膜的微觀結構與應力研究04-26
Fe3+催化氧化S(Ⅳ)反應機理初探04-26